[1]陈 燕.二次同步电压阳极氧化法制备TiO2纳米管的研究[J].绵阳师范学院学报,2018,(08):47-50.[doi:10.16276/j.cnki.cn51-1670/g.2018.08.009]
 CHEN Yan.Study on TiO2 Nanotube Arrays Prepared by Second Anodization under the Same Voltage[J].Journal of Mianyang Normal University,2018,(08):47-50.[doi:10.16276/j.cnki.cn51-1670/g.2018.08.009]
点击复制

二次同步电压阳极氧化法制备TiO2纳米管的研究(PDF)
分享到:

《绵阳师范学院学报》[ISSN:1672-612X/CN:51-1670/G]

卷:
期数:
2018年08期
页码:
47-50
栏目:
物理与电子信息技术
出版日期:
2018-08-07

文章信息/Info

Title:
Study on TiO2 Nanotube Arrays Prepared by Second Anodization under the Same Voltage
文章编号:
1672-612X(2018)08-0047-04
作者:
陈 燕
绵阳师范学院数理学院, 四川绵阳 621006
Author(s):
CHEN Yan
School of Mathematics and Physics, Mianyang Teachers' College, Mianyang Sichuan 621006
关键词:
TiO2 纳米管阵列 阳极氧化 扫描电镜
Keywords:
TiO2 NTAs Anodization SEM
分类号:
TN204; TN213;
DOI:
10.16276/j.cnki.cn51-1670/g.2018.08.009
文献标志码:
A
摘要:
论文研究了在钛金属薄片上采用电化学二次阳极氧化法制备出直径约为40 nm 的TiO2纳米管阵列.样品分别采用二次同步电压法和二次非同步电压法制备,并用电流加以控制.最后用扫描电镜扫描拍摄其微结构.结果发现采用二次阳极氧化法制备的纳米管阵列管状结构均为明显.此外,采用二次同步电压法制备的薄膜表面更是呈孔洞状结构, 且更加平整.
Abstract:
This paper presented The TiO2 nanotube arrays(NTAs)about diameter 40 nm which was prepared by electrochemically second anodization based on the titanium foil. The preparation process was under the same and various voltage than before respectively, and it controlled by the current. Finally, the microstructure of the samples was characterized by scanning electron microscopy(SEM). The results showed that all the tubular structure of TiO2 NTAs prepared by second anodization was very obviously. Furthermore, the surface of that film prepared under same voltage had a pore-like structure, and more smoothly as well.

参考文献/References:

[1] GONG D,GRIMES C A,VARGHESE O K,et al.Titanium Oxide Nanotube Arrays Prepared by Anodic Oxidation[J].Journal of Materials Research,2011,16(12):3331-3334.
[2] JUN Y,JONG W,PARKWB H,et al.The Preparation of Highly Ordered TiO2 Nanotube Arrays by an Anodization Method and Their Applications[J].Chemical Communications,2012,48(52):6456.
[3] TIAN Y,HU C,HE X,et al.Titania Nanotube Arrays for Light Sensor and UV Photometer[J].Sensors and Actuators B:Chemical,2010,144(1):203-207.
[4] KANG Q,LU Q Z,LIU S H,et al.A Ternary Hybrid CdS/Pt-TiO2 Nanotube Structure for Photoelectrocatalytic Bactericidal Effects on Escherichia coli[J].Biomaterials,2010,31(2):3317-3326.
[5] CAI Q,PAULOSE M,VARGHESE O K,et al.The effect of electrolyte composition on the fabrication of self-organized titanium oxide nanotube arrays by anodic oxidation[J].Journal of Materials Research,2005,20(1):230-236.
[6] PAULOSE M,SHANKAR K,YORIYA S,et al.Anodic growth of highly ordered TiO2 nanotube arrays to 134 mm in length[J].The Journal of Physics Chemistry B,2006,110(33):16179-16184.
[7] PAULOSE M,PRAKASAM H E,VARGHESE O K,et al.TiO2 Nanotube arrays of 1,000 mm in length by anodization of titanium foil: Phenol red diffusion[J].The Journal of Physics Chemistry C,2007,111(41):14992-14997.
[8] CHEN Y,ZHANG G W,DONG Z M,et al.Fabrication of Au nanoparticle/ double-walled carbon nanotube film/TiO2 nanotube array/Ti heterojunctions with low resistance state for broadband photodetectors[J].Physica B,2017,508(12):1-6.
[9] PRAKASAM H E,SHANKAR K,PAULOSE M,et al.A new benchmark for TiO2 nanotube array growth by anodization[J].The Journal of Physics Chemistry C,2007,111(20):7235-7241.
[10] ZHANG G W,SUN J L,WEI J Q,et al.Significantly Enhanced Photoresponse in Carbon Nanotube Film/TiO2 Nanotube Array Heterojunctions by Pre-Electroforming[J].Nanotechnology,2013,24(46):465203-465210.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期: 2018- 04-24
基金项目:绵阳师范学院科研项目(MYSY2017JC10).
作者简介:陈燕(1973- ),女,四川宜宾人,副教授,硕士,研究方向:光电材料及器件.
更新日期/Last Update: 2018-08-07